| Place of Origin: | China |
|---|---|
| Brand Name: | Kedo |
| Certification: | REACH; RoHs; FDA; ISO;OEKO-Tex |
| Model Number: | SY1018 |
| Minimum Order Quantity: | 200Kg |
| Price: | Us dollar 9.5-11/KG |
| Packaging Details: | one bucket at 20KG each or barrels if big quantity |
| Delivery Time: | 3-5 days |
| Payment Terms: | L/C, T/T, Western Union |
| Supply Ability: | 300 tons/ month |
| Category: | Liquid Silicone Rubber/LSR | Material: | Organic Silicone |
|---|---|---|---|
| Application: | Used For Heat Transfer Printing | Suitable Fabric: | First Screen Print On PET Film Sheet Then Heat Transfer To Fabric |
| Characteristics: | Doesn't Stratify Overnight, Easily Separate From PET Film Sheet And Strong Fasteness With Fabric, Excellent Elastic Rebound | Usage: | Mixed With Catalyst At Ratio Of 10:1 |
| High Light: | LSR heat transfer printing ink,REACH screen printing ink,REACH heat press ink |
||
Heat Transfer Printing Silicone Printing Rubber
Production Specification
| Product Name: | Heat Transfer Printing Silicone Printing Rubber |
| MOQ: | 200kg |
| Delivery Method: | Shipping, Air Freight, Express such as Dhl, ups, fedex, Or Ex Works |
| Sample time: | 3-5 working days |
| Lead time: | 10-15 days after confirm Sample |
| Delivery time: | 3~5 days via dhl door to door service |
| Payment terms: | TT Bank transfer, L/C in sight, Western Union |
| Models: | As per required |
| Size: | 1kg,2kg,5kg,20kg Or customized |
Product Description:
1. Ratio: this kind of silicone KD-SY1018 mixed with catalyst 1 a ratio of 10: 1
2. Production usage: For thick silicone heat transfer print
3. Advantages: Easily separate from PET film sheet and strong fasteness with fabric, excellent elastic rebound, no crack, seep or peel off.
Topic about making Reverse heat transfer silicone
Preparaion: Heat transfer printing silicone (code KD-SY1018), #1 or #3 Catalyst, Crosslinker #2A and catalyst #2B, Heat melt glue and PET film sheet.
Step 1: Mix heat transfer silicone SY1018 with catalyst at a ratio of 10:1, and print on PET film sheet for any thickness that you would like to have. Everytime you print silicone needs baking to surface dry.
Step 2: Mix Crosslinker Special#2A with 2B at a ratio of 1:1, then print one or two times, NO baked (If bake may not stick with heat melt glue)
Step 3: Print heat melt glue 5-8 times to surface dry.
Step 4: Leave it for 4 hours and then put in oven and bake with 120 degree centigrade for an hour.
Step 5: Press it together with cloth at 160 degree centigrade for 15 sec then the pattern will be tranfered on cloth.
FAQs
1.What is your sample making time?
Normally is 5-10 days
2.What is your MOQ?
Normally our MOQ is 200pcs/model/color except some special material required.
3.Can I get samples?
Yes, for sure.Sample fee will be refunded when the bulk order meets MOQ.
4.For Bulk order, what is your delivery UT?
L/T will be different per different model, style, material or Qty, but normally will be kept within 20-26days since order released.
5.What is the payment term of your company?
T/T, Western Union, 40%deposit + 60%balance paid before shipment.
6.What else services you can provide compare with other suppliers?
We can support our customer for small orders Viar which meet MOQ;We will show the newest design fashion product/picture/wearing picture to our
Customer.Help customer to sell more & build brand by full
Support four professional team.
7.How about your production capacity?
We have 3 production lines and can finish 500,000 pcsper month.
8.If I have my own design, can you make it?
Yes, we do both OED and ODM, just please send your design and requirements (size, color, etc), we will give you evaluation and quotation within 2 days.
9.What is your after sales service?
We will have full inspection before orders ship out, but once you find any problem, pis give us feedback within 2 days of receipt of the goods, our sales team will contact with you within 48 hours.
10.Do you have an exchange & return policy of defective items?
If the defectives are caused by material/ manufacture, we will provide free replacement service.